Convective heat transfer enhancement using Carbon nanofibers (CNFs): influence of amorphous carbon layer on heat transfer performance

Author(s)

Taha, T.J.; Lefferts, Leon; van der Meer, Theo;

Identification

MNHMT2013-22196

ISBN

DOI

Publication date

2013-11-14

Number of pages

10

Full text

PDF

Abstract

In this work, an experimental heat transfer investigation was carried out to investigate the combined influence of both amorphous carbon (a-C) layer thickness and carbon nanofibers (CNFs) on the convective heat transfer behavior. Synthesis of these carbon nano structures was achieved using catalytic chemical vapor deposition process (CCVD) on a 50 µm nickel wire at 650˚C. Due to their extremely high thermal conductivity, CNFs are used to augment/modify heat transfer surface. However, the inevitable layer of a-C that occurs during the synthesis of the CNFs layer exhibit low thermal conductivity which may result in insulating the surface. In contrast, the amorphous layer helps in supporting and mechanical stabilizing of the CNFs layer attachment to the polycrystalline nickel (Ni270) substrate material. To better understand the influences of these two layer on heat transfer, the growth mechanism of the CNFs layer and the layer of carbon is investigated and growth model is proposed. The combined impact of both a-C and CNFs layer on heat transfer performance is studied on three different samples which were synthesized by varying the deposition period (16 min, 23min and 30 min). The micro wire samples covered with CNF layers were subjected to a uniform flow from a nozzle. Heat transfer measurement was achieved by a controlled heat dissipation through the micro wire to attain a constant temperature during the flow. This measurement technique is adopted from hot wire anemometry calibration method. Maximum heat transfer enhancement of 18% was achieved. This enhancement is mainly attributed to the surface roughness and surface area increase of the samples with moderate CNFs surface area coverage on the sample.